HDPE 2001
| Color: | Black | |
| Composition | 100% HDPE mould-type material | |
| MFI (190 C/2.16 kg): | 2,5 – 5,5 g/10 min | |
| Suggested field of use: | Moulding, production of pallets, crates |
HDPE 2004 640 V
| Color: | Black | |
| Composition: | 60% HDPE, 40% LDPE | |
| MFI (190 C/5 kg): | 1,0-3,0 g/10 min | |
| Suggested field of use: | 1,0-3,0 g/10 min |
HDPE 2005
| Color: | Black | |
| Composition: | 100% HDPE | |
| MFI (190 C/2.16 kg): | 1,5-2,5 g/10 min | |
| Suggested field of use: | Production of bottle caps, pallets |
HDPE 2006
| Color: | Black | |
| Composition: | 100% extruder-type waste | |
| MFI (190 C/5 kg): | 0,5-1,5 g/10 min | |
| Suggested field of use: | Production of bottle blowing, protective tubes |
HDPE 2007 (pretreated) FL 01
| Color: | Non-coloured | |
| Composition: | 100% extruder-type polyolefin (PO) waste | |
| MFI (190 C/5 kg): | 1,5-3,0 g/10 min | |
| Suggested field of use: | Blowing of plastic bottles, production of pallets |
HDPE 2009
| Color: | Dark grey | |
| Composition: | 60% HDPE + 40% LDPE | |
| MFI (190 C/2,16 kg): | 2,0-4,0 g/10 min | |
| Suggested field of use: | Production of dustbins |
HDPE 2010 or 2013
| Color: | Mixed or black | |
| Composition: | Die-cast-type polyolefin (PO) waste | |
| MFI (190 C/2,16 kg): | 1,5-3,0 g/10 min | |
| Suggested field of use: | Die-casting, production of crates, grass lattices |
HDPE 2011 730V
| Color | Black | |
| Composition: | 70% waste type HDPE extruder + 30% LDPE | |
| MFI (190 C/5 kg): | 0,6-3,0 g/10 min | |
| Suggested field of use: | production of protective tubes |
LDPE 4001
| Color: | Dark grey | |
Composition: |
80% LDPE, 20% HDPE | |
| MFI (190 C/2.16 kg): | 1.5-3.5 g/10 min | |
Suggested field of use: |
Moulding, production of mortar boxes and buckets |
LDPE 4002
Color: |
Grey |
|
Composition: |
35% HDPE, 65% LDPE | |
| MFI (190 C/2.16 kg): | 0.8-2,0 g/10 min | |
Suggested field of use: |
Blowing of plastic bottles up to 1-2 l bottles |
LDPE 4003
Color: |
Grey |
|
Composition: |
LDPE 50% – HDPE 50% | |
| MFI (190 C/2,16 kg): | 0,5-2,0 g/10 min | |
Suggested field of use: |
Bottle blowing with a bottle size of 1 to 5 litres |
LDPE 4004
Color: |
Characteristic colours / not covered |
|
Composition: |
100% LDPE high-clarity |
|
| MFI (190 C/2.16 kg): | 0,8-1,5 g/10 min | |
Suggested field of use: |
Foil blowing |
LDPE 4006
Color: |
Natural brown or grey/not covered |
|
Composition: |
100% LDPE high-clarity |
|
| MFI (190 C/2.16 kg): | 0,8-1,5 g/10 min | |
Suggested field of use: |
Foil blowing |
LDPE 4012
Color: |
Light grey |
|
Composition: |
80% LD+20% HD die-cast-type waste |
|
| MFI (190 C/2,16 kg): | 1,5-3,5 g/10 min | |
Suggested field of use: |
Mouldin, production of electric outlet boxes |
LDPE 4017
Color: |
White |
|
Composition: |
86% LDPE, 14% CaCO3 | |
| MFI (190 C/2.16 kg): | 2,0 – 4,0 g/10 min | |
Suggested field of use: |
Moulding, additive for foil production. |
PP 5005
Color: |
Grey |
|
Composition: |
100% extruder-type PP |
|
| MFI (230 C/2,16 kg): | 0,5-1,5 g/10 min | |
Suggested field of use: |
Extruding |
PP 5006
Color: |
Mixed |
|
Composition: |
100% PP | |
| MFI (230 C/2,16 kg): | 2,0-5,0 g/10 min | |
Suggested field of use: |
die-casting, additive for producing strapping bands |
PP 5007
- copolymer
Color: |
Black |
|
Composition: |
100 % PP die-casting waste + 5% filling material (talc) |
|
| MFI (230 C/2.16 kg): | 2,5-5,5 g/10 min | |
Suggested field of use: |
Moulding |
PP 5009 RD2
-
copolymer
Color: |
Black |
|
Composition: |
100% PP | |
| MFI (230 C/2.16 kg): | 1,5-2,5 g/10 min | |
Suggested field of use: |
Extruding, production of straps |
PS 6001-HIPS
Color: |
Black |
|
Composition: |
100% PS moulding material |
|
| MFI (200 C/5 kg): | 3.0-6.0 g/10 min | |
Suggested field of use: |
Moulding, plate extruding (2-4 mm) |